wood-filled filament is a composite of PLA with real wood particles (typically 10%) creating parts with authentic wood appearance and smell. Prints can be sanded, stained, and finished like real wood for decorative items. Larger 0.5mm+ nozzle recommended; wood content may vary slightly affecting color.

📊 Technical Specifications

Nozzle Temperature 195-210 °C
Bed Temperature 50-60 °C
Print Speed 30-80 mm/s *
Part Cooling Fan 80-100 % *
Max Volumetric Speed 10 mm³/s *
Drying Temperature 45 °C *
Drying Time 6 hours *
Enclosure Required No *
Tensile Strength (Yield) 50 MPa
Tensile Strength (Break) 40 MPa *
Tensile Modulus 2800 MPa *
Elongation at Break 3 %
Flexural Strength 70 MPa
Flexural Modulus 2800 MPa
Impact Strength (Izod) 30 J/m
Heat Deflection (0.45 MPa) 54 °C
Heat Deflection (1.8 MPa) 50 °C *
Glass Transition (Tg) 60 °C *
Melting Point 150-165 °C *
Density 1.1 g/cm³
Water Absorption (24h) 0.6 % *
Bed Adhesion PEI *

* Estimated values based on material family characteristics