Name: yxpolyer Wood Dark 1.75mm 1kg
Brand: yxpolyer
SKU: SLV-WOOD-DK-1K
Price: 3850 ISK
Availability: InStock

3.850 kr

3.850 kr

Wood-filled filament is a composite of PLA with real wood particles creating parts with authentic wood appearance and smell. Prints can be sanded

Nozzle Temperature	195-210 °C *
Bed Temperature	50-60 °C *
Print Speed	30-80 mm/s *
Part Cooling Fan	80-100 % *
Max Volumetric Speed	10 mm³/s *
Drying Temperature	45 °C *
Drying Time	6 hours *
Enclosure Required	No *
Tensile Strength (Yield, XY)	50 MPa *
Tensile Strength (Yield, Z)	22.5 MPa *
Tensile Strength (Break, XY)	40 MPa *
Tensile Strength (Break, Z)	18 MPa *
Tensile Modulus (XY)	2800 MPa *
Tensile Modulus (Z)	1680 MPa *
Elongation at Break	3 % *
Flexural Strength (XY)	70 MPa *
Flexural Strength (Z)	38.5 MPa *
Flexural Modulus (XY)	2800 MPa *
Flexural Modulus (Z)	1820 MPa *
Impact Strength (Izod)	30 J/m *
Impact Strength (Unnotched, XY)	20 kJ/m² *
Impact Strength (Unnotched, Z)	8 kJ/m² *
Heat Deflection (0.45 MPa)	54 °C *
Heat Deflection (1.8 MPa)	50 °C *
Glass Transition (Tg)	60 °C *
Melting Point	150-165 °C *
Density	1.1 g/cm³ *
Hardness (Shore A)	75 *
Hardness (Shore D)	70 *
Hardness (Rockwell R)	95 *
Continuous Service Temp	50 °C *
Light Transmittance	0 % *
Dielectric Strength	15 kV/mm *
Impact Strength (Charpy)	5 kJ/m² *
Elongation at Yield	2 % *
Mold Shrinkage	0-0 % *
Water Absorption (24h)	0.6 % *
Flammability Rating	HB *
Bed Adhesion	PEI *

* Estimated values based on material family characteristics