yxpolyer PC-ABS Black 1.75mm 1kg

yxpolyer PC-ABS Black 1.75mm 1kg

5,800 kr
Skip to product information
yxpolyer PC-ABS Black 1.75mm 1kg
  • yxpolyer PC-ABS Black 1.75mm 1kg
  • yxpolyer PC-ABS Black 1.75mm 1kg
yxpolyer PC-ABS Black 1.75mm 1kg

yxpolyer PC-ABS Black 1.75mm 1kg

5,800 kr

yxpolyer PC-ABS is a high-performance alloy combining the strength and heat resistance of polycarbonate with the toughness and printability of ABS. It features UL94 V-0 standard flame retardancy, making it ideal for fire-resistant structural components, electrical power tool housings, automotive parts, and electronic enclosures requiring high dimensional stability and heat resistance. Requires an enclosure and high printing temperatures.

📊 Technical Specifications

Nozzle Temperature 260-280 °C
Bed Temperature 80-100 °C *
Print Speed 30-180 mm/s *
Part Cooling Fan 0 % *
Max Volumetric Speed 14 mm³/s *
Drying Temperature 80 °C *
Drying Time 6 hours *
Enclosure Required Yes *
Tensile Strength (Yield, XY) 50 MPa
Tensile Strength (Yield, Z) 37.5 MPa *
Tensile Strength (Break, XY) 42 MPa *
Tensile Strength (Break, Z) 31.5 MPa *
Tensile Modulus (XY) 2049 MPa *
Tensile Modulus (Z) 1639.2 MPa *
Elongation at Break 8 %
Flexural Strength (XY) 82 MPa
Flexural Strength (Z) 69.7 MPa *
Flexural Modulus (XY) 2049 MPa
Flexural Modulus (Z) 1680.2 MPa *
Impact Strength (Izod) 210 J/m *
Impact Strength (Unnotched, XY) 80 kJ/m² *
Impact Strength (Unnotched, Z) 56 kJ/m² *
Heat Deflection (0.45 MPa) 100 °C
Heat Deflection (1.8 MPa) 92 °C
Glass Transition (Tg) 105 °C *
Melting Point 225 °C
Density 1.2 g/cm³
Hardness (Shore A) 53.6 *
Hardness (Shore D) 89
Hardness (Rockwell R) 110 *
Continuous Service Temp 95 °C *
Light Transmittance 5 % *
Dielectric Strength 19 kV/mm *
Impact Strength (Charpy) 20 kJ/m² *
Elongation at Yield 5 % *
Mold Shrinkage 0-0 % *
Water Absorption (24h) 0.3 % *
Flammability Rating V-0
Bed Adhesion ABS Adhesive *

* Estimated values based on material family characteristics

📋 Documentation