HIPS (High Impact Polystyrene) serves dual purposes: as a support material soluble in limonene (d-limonene citrus cleaner) and as a lightweight structural material. When used as a support it dissolves away cleanly leaving ABS/ASA parts intact; as a primary material it offers good machinability and matte white finish. Requires enclosed printer.

📊 Technical Specifications

Nozzle Temperature 230-250 °C *
Bed Temperature 100-110 °C *
Print Speed 40-60 mm/s *
Part Cooling Fan 0 % *
Max Volumetric Speed 14.4 mm³/s *
Drying Temperature 70-80°C *
Drying Time 2 hours *
Enclosure Required Yes *
Tensile Strength (Yield, XY) 22.8 MPa
Tensile Strength (Yield, Z) 10.3 MPa *
Tensile Strength (Break, XY) 19.3 MPa
Tensile Strength (Break, Z) 8.7 MPa *
Tensile Modulus (XY) 1860 MPa
Tensile Modulus (Z) 1116 MPa *
Elongation at Break 50 %
Flexural Strength (XY) 44.8 MPa
Flexural Strength (Z) 24.6 MPa *
Flexural Modulus (XY) 2140 MPa
Flexural Modulus (Z) 1391 MPa *
Impact Strength (Izod) 240.0 J/m
Impact Strength (Unnotched, XY) 72 kJ/m² *
Impact Strength (Unnotched, Z) 28.8 kJ/m² *
Heat Deflection (0.45 MPa) 87 °C *
Heat Deflection (1.8 MPa) 72.8 °C
Glass Transition (Tg) 100 °C *
Melting Point 90-130 °C *
Density 1.0 g/cm³
Hardness (Shore A) 65 *
Hardness (Shore D) 39.9 *
Hardness (Rockwell R) 87.8 *
Continuous Service Temp 70 °C *
Light Transmittance 0 % *
Dielectric Strength 18 kV/mm *
Impact Strength (Charpy) 18 kJ/m²
Elongation at Yield 2 % *
Mold Shrinkage 0-0 %
Water Absorption (24h) 0.1 % *
Flammability Rating HB
Bed Adhesion ABS Adhesive *

* Estimated values based on material family characteristics